1.說明
BGA氣泡小，空洞率低，印刷好，,手機(jī)，電腦主板,尤其是密間距元件印刷性較好。
品質(zhì)：
化學(xué)成分：
該Solder Paste 使用高品質(zhì)真圓球形粉末,其成分如 表-1所列： 表-1 金屬成分
|
Sn%
|
|
Ag%
|
Cu%
|
Pb%
|
Sb%
|
|
Bi%
|
|
|
Zn%
|
Fe%
|
|
Al%
|
As%
|
|
Cd%
|
|
|
余量
|
|
3.0±0.2
|
0.5±0.05
|
＜0.05
|
≤0.10
|
|
≤0.05
|
|
≤0.001
|
≤0.02
|
|
≤0.001
|
≤0.03
|
|
＜0.002
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
粉末顆粒范圍:№粉末尺寸(μm)及目數(shù)相應(yīng)代號 ①45~25(-325/500)C ②38~20(-400/635)D
2.2 特性：
|
|
|
該Solder Paste 的特性如表-2所列：
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
表-2 特性值
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
項
|
|
目
|
|
|
|
特 性 值
|
|
|
|
試 驗 方 法
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Flux %
|
|
|
11.5 ± 0.5
|
|
|
JIS Z 3197 - 8.1.2
|
|
|
|
|
助焊劑含量 %
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Chlorine conten in Flux %
|
|
0.08 ± 0.02
|
|
|
|
電位差自動滴定
|
|
|
|
|
氯素含量 %
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Copper plate Corrosion
|
|
|
未發(fā)生
|
|
|
|
JIS Z 3284 - 4
|
|
|
|
|
銅板腐蝕
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Water solution resistance Ω cm
|
|
> 5×104
|
|
|
|
|
|
|
|
|
|
|
|
水溶液阻抗 Ω cm
|
|
|
|
|
|
JIS Z 3197 - 8.1.1
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Insulation resistance
|
Ω cm
|
40℃
|
|
> 1×10
|
11
|
|
|
|
JIS Z 3284 - 3
|
|
|
|
絕緣阻抗 Ω cm
|
|
|
|
|
|
|
|
|
|
90%
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Migration
|
|
|
|
無
|
|
|
|
|
|
JIS Z 3284 - 14
|
|
|
|
|
遷移試驗
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Spreading %
|
|
|
> 80
|
|
|
|
|
JIS Z 3197(- 8.3.1.1
|
|
|
擴(kuò)散率 %(CuO板)
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Viscosity
|
Pa.s
|
|
|
190±30
|
|
Malcom PCU-205: 10rpm 3min
|
|
|
|
粘度 Pa.s
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Melting
|
point ℃
|
|
|
217-221
|
|
|
|
|
|
-
|
|
|
|
|
|
融點 ℃
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Solder ball test
|
|
|
|
等級1~3
|
|
|
|
JIS Z 3284 -11
|
|
|
|
|
錫球試驗
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
適宜印刷間距
|
|
GMC-M305-C-885 : ≥0.4
|
|
|
|
-
|
|
|
|
|
|
(mm)
|
|
|
GMC-M305-D-885 : ≥0.3
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Slump-in-printing
|
|
|
|
0.2mm
|
|
|
|
JIS Z 3284 - 7
|
|
|
|
|
印刷塌陷
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Slump-in-heating
|
|
|
|
0.3mm
|
|
|
|
JIS Z 3284 - 8
|
|
|
|
|
加熱塌陷
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Tackiness(time tacking force is
|
|
|
24hr
|
|
|
|
|
|
JIS Z 3284 - 9
|
|
|
|
粘著性(1.2N以上保持時間)
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
流動特性
|
|
|
0.50~0.70
|
|
|
|
JIS Z 3284 - 6
|
|
|
|
Fluidity characteristic(Ti)
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
3.產(chǎn)品特點：
3.1本產(chǎn)品采用敝司最新開發(fā)的助焊劑而具有優(yōu)異的粘度穩(wěn)定性;常溫(∠35℃)下保質(zhì)期為2個
月,方便運輸及保管;
3.2本產(chǎn)品在高溫高濕環(huán)境下,連續(xù)使用粘度穩(wěn)定性非常佳;
3.3連續(xù)印刷7天,本產(chǎn)品仍可保持優(yōu)良的性能,減少消耗量;
3.4有效減少空洞率及錫珠;
3.5有效抑制BGA虛焊的發(fā)生.